May 18, 2024

Synthesis of a nitrogen doped reduced graphene oxide based ceramic polymer composite nanofiber film for wearable device applications

Scientific Reports volume 12, Article number: 15583 (2022) Cite this article In this study, piezoelectric composite nanofiber films were fabricated by introducing nitrogen-doped-reduced-graphene-oxide

Scientific Reports volume 12, Article number: 15583 (2022) Cite this article

In this study, piezoelectric composite nanofiber films were fabricated by introducing nitrogen-doped-reduced-graphene-oxide as a conductive material to a P(VDF-TrFE) polymer and a BiScO3–PbTiO3 ceramic composite employing an electrospinning process. Nitrogen was doped/substituted into rGO to remove or compensate defects formed during the reduction process. Electro-spinning process was employed to extract piezoelectric composite nanofiber films under self-poling condition. Interdigital electrodes was employed to make planner type energy harvesters to collect electro-mechanical energy applied to the flexible energy harvester. From the piezoelectric composite with interdigital electrode, the effective dielectric permittivity extracted from the conformal mapping method. By introducing BS–PT ceramics and N-rGO conductors to the P(VDF-TrFE) piezoelectric composite nanofiber films, the effective dielectric permittivity was improved from 8.2 to 15.5. This improved effective dielectric constant probably come from the increased electric flux density due to the increased conductivity. Fabricated interdigital electrode using this thin composite nanofiber film was designed and tested for wearable device applications. An external mechanical force of 350 N was applied to the composite nanofiber-based energy harvester with interdigital electrodes at a rate of 0.6 Hz, the peak voltage and current were 13 V and 1.25 μA, respectively. By optimizing the device fabrication, the open-circuit voltage, stored voltage, and generated output power obtained were 12.4 V, 3.78 V, and 6.3 μW, respectively.

Piezoelectric composite materials based on polymers and ceramics have attracted notable attention because of their superior electrical and mechanical properties, such as flexibility, piezoelectricity, and robustness1,2,3. In general, piezoelectric polymers are based mainly on PVDF and P(VDF-TrFE) materials4,5. Their electrical properties can be enhanced by adding piezoelectric ceramics to make piezoelectric composite structures. Although piezoelectric composites have been realized, limitations in improving their piezoelectric properties exist owing to their resistive behaviors. To overcome these limitations, conductive materials can be added to piezoelectric composites to improve their electrical properties. Two-dimensional (2D) rGO is widely employed as a conducting material which can be easily mixed with other components to improve electrical and mechanical properties6,7,8. Therefore, introducing rGO into piezoelectric polymers including PVDF and P(VDF-TrFE), can result in improved piezoelectric properties9,10. However, many defects are induced during the reduction process of rGO, which can hinder its electron transport properties. These defects can be very detrimental for piezoelectric applications because they disrupt the electric field11,12. rGO has been extensively investigated for two dimensional functional device applications owing to its high electrical conductivity and flexibility13,14. However, defects originating from the reduction process diminish electrical properties of rGO. To overcome diminished conductive properties, N was doped/substituted into two dimensional rGO. Doping/substitution of N can overcome defects in rGO, resulting in a higher electrical conductivity6.

Piezoelectric nanofiber films based on polymer and ceramic ingredients process several advantages compared to other composite structures, such as flexibility and piezoelectricity13,15. A nanofiber film has a superior flexibility owing to its high aspect ratio compared to other composite and ceramic materials. An electrospinning process was designed and adopted to fabricate reliable nanofiber and composite nanofiber structures. Electrospinning is a technique that produces nanofibers of polymers, ceramics, and metals by applying an electric field. This process can form nanofibers from complex molecules and can operate at low temperatures16,17.

Electrospinning process was employed to fabricate N-rGO doped/substituted piezoelectric composite nanofiber based on P(VDF-TrFE) polymer and BS–PT ceramics. Electrospinning process has many advantages compared with other physical fabrication processes, since it can be low-cost fabrication process by extracting piezoelectric composite nanofiber under self-poling condition. Moreover, highly conductive N-rGO and piezoelectric composite nanofibers can be well mixed during the preparation process before electro-spinning process. As a result, N-rGO doped piezoelectric composite nanofiber can be applied to various different types of wearable device applications.

The main advantage of this synthesized N-rGO with composite nanofiber is that increased conductivity from N-rGO compared with that of rGO. Nitrogen plays role of removing defects in the rGO or substitute with carbon in the rGO materials. Therefore, this increased conductivity can improve floating electrode effects in the piezoelectric composite materials. Also, the representative results of this manuscript compared with other papers can be summarized as follow. N-rGO-doped piezoelectric composite nanofiber composites based on polymer and BiScO3–PbTiO3 were fabricated in the form of planar piezoelectric energy harvesters with interdigital electrodes. It was the first time to report the improved floating electrode effects based on the planner type piezoelectric energy harvesters.

For the device applications, interdigital electrodes were designed and employed to N-rGO doped/substituted piezoelectric composite nanofiber based on P(VDF-TrFE) polymer and BS–PT ceramics. Almost all wearable devices are based on the planner type structure, classical vertical type electrode cannot be applied for the device applications. Applied mechanical forces can be converted to the electrical energies through the interdigital electrode on the piezoelectric nanofibers. The effective dielectric permittivity can be simulated and calculated by employing the conformal mapping process. By extracting the different values of effective dielectric permittivity of piezoelectric composite nanofibers, we believe that N-rGO doped piezoelectric nanofibers with planner type electrode can be applied for the various wearable device applications.

In this study, composite nanofiber films comprising N-rGO-incorporated P(VDF-TrFE) polymers and BiScO3–PbTiO3 ceramics were prepared using electrospinning. Flexible piezoelectric energy harvesters based on these composites were investigated for use in wearable electronic applications.

Bi2O3, Sc2O3, PbO and TiO2 powers were employed as the raw materials. By considering the volatilization degree of Bi2O3 elements, 0.01 mol excessed Bi was added to BS–PT compositions. The mixture was milled with stabilized zirconia ball. Then, the mixture were calcined and sintered in powder form. The sintered powders were controlled to have less than 50 μm. Finally, the powders were ball-milled by planetary milling.

Nitrogen doped rGO was prepared by a modified Hummers method18. Graphite and NaNO3 powder were added to H2SO4 by stirring in bath. KMnO4 was then added slowly to the solution. Deionized water was added to the solutions, and stirred for 1 h, followed by the addition of 10 mL of H2O2. To eliminate oxidant ions and other inorganic impurities, distilled water and 1:10 HCl aqueous solution were added and centrifuged, and the mixture was washed several times. Hydrazine hydrate was added to the solution to fabricate rGO. To produce nitrogen-doped rGO, graphene oxide and NH3NO3 were added to ethanol solution and stirred. To remove the ethanol, the solution was heated to 60 °C. The dried mixture was calcined and washed with deionized water and ethanol.

Figure 1a shows a schematic of the fabrication process of a flexible piezoelectric energy harvester based on a composite nanofiber film. To prepare the composite solution, P(VDF-TrFE) (Solvay Co. Ltd.), acetone (Sigma-Aldrich Co. Ltd. , purity: 99.5%), and N, N-dimethylformamide (DMF, Sigma-Aldrich Co., Ltd., purity: 99.8%) were mixed in a weight ratio of 2:5:5 and stirred for 24 h. Then, BiScO3–PbTiO3 (BS-PT) nanoparticles (30 wt.%) and N-rGO powders (5 wt.%) were added to the mixture and stirred. Finally, P(VDF-TrFE) and P(VDF-TrFE)/BS-PT composite solutions were obtained. The composite solution was loaded into a 10 mL plastic syringe with a 21 G metal nozzle and then electrospun. The electrospinning process was performed using an electric field of 1.2 kV/cm, feed rate of 1 mL/h, distance between the needle tip and the collector of 12 cm, and substrate temperature of 55 °C.

Diagrams of fabrication processes for (a) nanofiber composite film and (b) piezoelectric energy harvester.

As shown in Fig. 1a, the electrospinning process was applied to a polyimide substrate coated with an interdigital electrode to fabricate an energy harvesting device based on composite nanofiber films. Figure 1b shows a schematic of the fabrication process for a piezoelectric energy harvester with interdigital electrodes. The interdigital electrode had twenty pairs of Cu fingers with sizes and gaps of 100 µm. Interdigital electrodes are effective for measuring planar capacitances; therefore, these electrodes are useful in energy harvesting applications, where a large number of piezoelectric charges are developed and retained. After this process, polydimethylsiloxane (PDMS) was used to encapsulate the device for stability and protection. The crystal structures of the samples were determined via X-ray diffraction (XRD, Bruker-AXS; New D8-Advance). Field-emission scanning electron microscopy (FE-SEM, Carl Zeiss, SIGMA HD) was performed to study microstructures of composite nanofiber films. The generated output voltage and current were analyzed using an oscilloscope (DSO-X2002A, Agilent Technologies) and a Femto/Picoammeter (B2981A, Agilent Technologies). The stored voltage of the energy harvesting device was measured in the external capacitor of a full-bridge rectifier.

Figure 2a shows FE-SEM image of P(VDF-TrFE)/BS-PT/N-rGO composite nanofiber films. The composite nanofiber was long and smooth, with a diameter of approximately 800 nm. Sub-micrometer particles were well dispersed on the nanofiber, which suggests a high compatibility between sub-micron-sized functional ceramic particles and the N-rGO-doped P(VDF-TrFE) matrix. In the Fig. 2b, EDS compositional analysis data were displayed with different colors. Different elemental compositions were detected. Composition of C, F, N, O, Bi, Sc, Pb, and Ti were distributed in P(VDF-TrFE)/BS-PT/N-rGO composite nanofiber films; the corresponding atomic and weight percentages are listed in Table 1.

(a) FE-SEM image of P(VDF-TrFE)/BS-PT/N-rGO nanofiber composite film, (b) EDS data for the P(VDF-TrFE)/BS-PT/N-rGO nanofiber composite film with different composite (c) Schematic diagram of floating electrode component of N-rGO in nanofiber structure, (d) clear TEM images of TEM images of P(VDF-TrFE)/BS-PT/N-rGO film.

Figure 2c shows a schematic of floating electrodes of conductive N-rGO particles contained in the composite nanofiber structure. Dispersed conductive N-rGO act as floating electrodes in composites, which help collect charges from piezoelectric materials.

Figure 2d shows the TEM images measured in the mass-thickness contrast mode. In the bright field image mode Fig. 2c, the ceramic parts can be seen in the dark images on the while, the polymer part can be seen in the bright color. Therefore, we expect that piezoelectric BS–PT ceramic particles and conductive N-rGO floating electrodes in composite nanofiber structures will enhance the output power of energy harvesters.

X-ray diffraction (XRD) patterns of P(VDF-TrFE), P(VDF-TrFE)/BS–PT, and P(VDF-TrFE)/BS–PT/N-rGO composite nanofiber films is shown in Fig. 3. P(VDF-TrFE) films show peaks of the β phase (110/200) at 2θ = 19.8°. This β-phase polymer structure has ferroelectric properties resulting from the atomic arrangement. XRD patterns of P(VDF-TrFE)/BS–PT composite nanofiber films indicated the formation of the β-phase polymer structure; however, the crystallinity was lower than that of the P(VDF-TrFE)/BS–PT composite film. The amount of the β-phase polymer appeared to decrease during the fabrication process. However, a small amount of the β-phase polymer remained after the processing. BS–PT peaks in XRD measurements indicated that BS–PT piezoelectric nanoparticles were well dispersed in P(VDF-TrFE)/BS–PT composite nanofiber films. This result suggests that BS–PT ceramic nanoparticles were not only effectively dispersed in P(VDF-TrFE) nanofibers but were also undisturbed during the electrospinning process.

XRD patterns of P(VDF-TrFE), P(VDF-TrFE)/BS-PT, and P(VDF-TrFE)/BS-PT/N-rGO nanofiber films.

Figure 4a shows the XPS survey scan spectrum of N-rGO and the chemical composition of each element. Carbon, nitrogen, and oxygen peaks appeared around 285.2 eV, 399.5 eV, and 533.0 eV, and the atomic ratios were confirmed to be 73.9%, 6.1%, and 20.0%, respectively.

(a) XPS survey and (b) N 1 s scan of synthesized N-rGO and (c) sheet resistance according to rGO, N-rGO deposition temperature.

Figure 4b shows the bonding state of N 1 s. In N-rGO, the N 1 s peak can be separated into pyridinic-like N (398.5 eV) which represents the nitrogen located on the 6-membered ring, pyrrolic-like N (400.1 eV) which represents the nitrogen located on nitrogen in a five-membered ring, and graphitic-like N (402.7 eV) peaks19. Pyridinic-like N, pyrrolic-like N, and graphitic-like N binding ratio were approximately 21.2%, 51.3%, and 27.5%, respectively.

Figure 4c shows sheet resistance of rGO and N-rGO films after the rapid thermal annealing (RTA) process. As a result of performing the RTA process at 700 °C, the sheet resistance the lowest value of the rGO film was 5.29 kΩ/sq. The N-rGO film was 3.37 kΩ/sq. At all processing temperatures, the sheet resistance of the N-rGO film was lower than that of the rGO film. Therefore, due to the high conductivity of N-rGO, the N-rGO-based piezoelectric composite nanofiber films are expected to have improved electrical properties and piezoelectricity.

Figure 5a shows a schematic of a flexible PI-substrate-based composite nanofiber energy harvester with interdigital electrodes. A conformal mapping technique was applied to extract the effective dielectric permittivity from the analyzed capacitance of the interdigital electrode. Conformal mapping analysis allows the electric field distribution to be changed from rectangular to circular coordinates. As a result, effective dielectric permittivity of the composite nanofiber film and the PI substrate, εn and εs, could be estimated, as shown in Fig. 5a. The indispensable condition for using a conformal mapping to a two-layered substrate is εn > εs. Otherwise, the electric field cannot be confined within the composite nanofiber layer. As shown in Fig. 5a, W is the finger width, G is the space between fingers, λ is the spatial wavelength of the interdigital capacitor (IDC), t is the thickness of the metal electrode pattern, and hn is the height of the nanofiber film and substrate. We obtained analytical models of the IDC following the work of Gevorgian20,21. Modified Igreja’s equations for capacitances of inner (CI) and outer (CE) electrodes were determined, as shown in Fig. 5b, where it was assumed that the substrate thickness was non-infinite and the air layer below the substrate was infinitely thick. Equations of the IDC can then be expressed as follows21:

where K is elliptical integrals defined bellow; k and k′ are argument of each elliptical integral defined below; \({C}_{I,n}\), \({C}_{I,s}\), \({C}_{E,n}\), and \({C}_{E,s}\) are interior and exterior electrode capacitances of the nanofiber film (n) and the substrate (s), respectively; L is the length of fingers; εn is the effective dielectric permittivity of the nanofiber film; and εs is the effective dielectric permittivity of the substrate. In addition, the relationship between moduli of elliptical integrals k and k' are as follows:

(a) Cross-section view of two-layer substrate for IDC, (b) equivalent circuit for IDC, and (c) effective dielectric permittivity of composite nanofiber films.

This conformal mapping analysis allowed for the effective dielectric permittivity to be calculated. The extracted dielectric constant, as shown Fig. 5c, was approximately 8.2, 12.3, 13.9 and 15.5 for P(VDF-TrFE), P(VDF-TrFE)/BS–PT, P(VDF-TrFE)/BS–PT/rGO and P(VDF-TrFE)/BS–PT/N-rGO, respectively. The higher effective dielectric permittivity of P(VDF-TrFE)/BS–PT/N-rGO was attributed to the floating electrode behavior, as described in Fig. 2b. The floating N-rGO electrode in the composite nanofiber causes charges to be more easily attracted and collected by interdigital electrodes. Therefore, the effective dielectric permittivity was improved owing to increased electric flux densities resulting from the increased charge in interdigital electrodes. In addition, due to the high conductivity of N-rGO, it can be seen that the formation of charges in the composite film is strengthened and the dielectric properties are improved compared to that of rGO.

Figure 6a shows a schematic of the measurement system for the energy harvester. The mechanical force system was connected to an energy harvester with a circuit system and was controlled by a computer. An external mechanical force of 350 N was applied to the composite nanofiber with interdigital electrodes at a rate of 0.6 Hz. The generated output power was recorded by the computer. Figure 6b,c show repeated positive and negative output voltages and currents generated during the continuous pushing and release of the external mechanical force for P(VDF-TrFE)/BS–PT/rGO, P(VDF-TrFE)/BS–PT/N-rGO. The generated open-circuit voltage and short-circuit current were measured and recorded. The peak voltage and current of the energy harvester based on the composite nanofiber film were 11.2 V and 1.09 μA in P(VDF-TrFE)/BS–PT/rGO, 13 V and 1.25 μA in P(VDF-TrFE)/BS–PT/N-rGO. Positive values of voltages and currents are attributed to the applied stress, while negative values are attributed to the release of stress; hence, negative values are always smaller in magnitude than positive values.

(a) Schematic of measurement system, and open-circuit voltage and short-circuit current of (b) P(VDF-TrFE)/BS-PT/rGO, (c) P(VDF-TrFE)/BS-PT/N-rGO energy harvester based on composite nanofiber films.

Figure 7a shows measured output voltages and currents of the energy harvester based on the composite nanofiber film with different loading resistances. To measure the generated output power of the energy harvesting system, a load resistor or capacitor was used to measure the maximum output power and energy. The maximum power density was obtained by optimizing the load resistance. By varying the load resistance, the output load current was decreased from 1.27 to 0.2 μA, and the output load voltage was increased from 0.15 to 13.2 V.

(a) Output voltage and current, (b) power, (c) stored voltage, and (d) reliability of nanofiber composite film energy harvester.

Figure 7b shows the output power generated by the energy harvester. The output power was calculated from the voltage and current across the load. The output voltage and current were measured at an external load resistance, ranging from 100 kΩ to 500 MΩ, that was connected to the composite nanofiber film energy harvester. The output power can be expressed as:

where IL and VL are the output current and voltage across the load resistance, respectively. As shown in Fig. 7b, the output power of the energy harvester first increased and then decreased. The maximum output power was 6.3 μW at an optimized load resistance of 37 MΩ, corresponding to a voltage of 9.27 V and a current of 0.68 μA. After this peak value, the generated output power decreased. Additionally, the power density can be expressed as:

The generated output power of the piezoelectric energy harvester based on the composite nanofiber film was 0.63 mW/cm3.

The load current can be expressed as:

where Rpiezo and RL are resistances of the composite nanofiber film and the load, respectively. Therefore, Eq. (5) can be expressed as:

The maximum value of PL occurs at the minimum value of the denominator, and therefore, the derivative of the denominator of PL can be expressed as:

Consequently, the maximum PL value occurs when Rpiezo = RL. In our study, the optimized load resistance was measured to be 37 MΩ, and therefore, according to the above formula, the resistance of the piezoelectric energy harvester, \({R}_{piezo}\), is estimated to be 37 MΩ.

Figures 7c,d show the stored voltage and reliability results of the energy harvester based on the composite nanofiber film. The stored voltage of the energy harvester increased up to 3.78 V when mechanical forces were applied. The output properties of composite nanofiber film were compared with other polymer/ceramic piezoelectric composites and are summarized in Table 222,23,24,25,26. As shown in the Table 2, compared with other researches, highly conductive N-rGO was introduced to piezoelectric composite nanofiber to improve electro-mechanical properties, which employed in the energy harvester. Therefore, the output energy from the energy harvester was increased by large margin compared with other recent result. The result was compared and listed in the Table 2.

Periodic external mechanical forces were applied to examine the reliability of the output performance of the composite nanofiber energy harvesting system. More than 1000 cycles of mechanical forces were applied to the composite-nanofiber-based energy harvester. The applied mechanical force was approximately 300 N at a rate of 1.5 Hz. The generated voltage was recorded simultaneously using an oscilloscope. The flexible piezoelectric energy harvester exhibited a stable output performance even under a constant external pressure. The results indicate that the energy harvester based on the composite nanofiber film exhibits an outstanding output performance without any fatigue.

Figure 8 shows output performance of wearable devices under different loading frequencies in P(VDF-TrFE)/BS–PT/rGO and P(VDF-TrFE)/BS–PT/N-rGO composite nanofiber films. As increasing the loading frequency, the output voltages and current were decreased. In P(VDF-TrFE)/BS–PT/rGO, the output voltages and current were decreased from 11.2 V, 1.09 μA to 7.2 V, 0.72 μA, and in P(VDF-TrFE)/BS–PT/N-rGO composite nanofiber film, it decreased from 13.3 V and 1.29 μA to 9.3 V and 0.91 μA. P(VDF-TrFE)/BS–PT/N-rGO showed better output performance than P(VDF-TrFE)/BS-PT/rGO at all loading frequencies. As a result, after stress relief, stress was applied before recovery, resulting in reduced output performance.

Open circuit voltage and short circuit current at 0.6, 1.2 and 1.8 Hz for (a), (b) P(VDF-TrFE)/BS-PT/rGO and (c), (d) P(VDF-TrFE)/BS-PT/N-rGO piezoelectric composite nanofiber films.

Figure 9 shows the measured output voltage and the manufactured device under daily life conditions. The fabricated device was tested under stepping, tapping, and clapping conditions. The output voltages were 16.7 V and 3.4 V in the stepped and pressed conditions of the device. When the hand was clapping, an output voltage of up to 7.3 V could be obtained, and a random output voltage is measured. This result is due to the irregular impact applied. The measurement conditions were operated at 23 °C, 47% temperature and humidity conditions.

Output voltage when (a) pressed with the heel, (b) hit with the finger, and (c) when clapped with the palm the device and (d) the fabricated device.

In this study, N-rGO-doped P(VDF-TrFE)/BiScO3–PbTiO3-based composite nanofiber films were prepared using electrospinning. Conductive N-rGO was doped as a floating electrode material for the P(VDF-TrFE) polymer and the BiScO3–PbTiO3 polymer-ceramic composite. In addition, by generated output power, the maximum value of power density could be calculated used impedance matching. This composite-nanofiber-based energy harvester showed an improved output power owing to floating electrode effects. An interdigital electrode, which is an effective electrode structure for use in wearable device applications, was designed and tested. The generated output power was maximized by optimizing the fabrication process and the interdigital electrode design. The obtained open-circuit voltage, stored voltage, and generated output power were 12.4 V, 3.78 V, and 6.3 μW, respectively. As a result, floating electrodes in the composite nanofiber improved the output power and the effective dielectric permittivity.

All data generated or analyzed during this study are included in this published article.

Kim, K. et al. 3D optical printing of piezoelectric nanoparticle-polymer composite materials. ACS Nano 8, 9799. https://doi.org/10.1021/nn503268f (2014).

Article CAS PubMed Google Scholar

Stuber, V. L. et al. Flexible lead-free piezoelectric composite materials for energy harvesting applications. Energ. Technol. 7, 177. https://doi.org/10.1002/ente.201800419 (2019).

Article CAS Google Scholar

Li, L., Xu, J., Liu, J. & Gao, F. Recent progress on piezoelectric energy harvesting: Structures and materials. Adv. Composites Hybrid Mater. 1, 478. https://doi.org/10.1007/s42114-018-0046-1 (2018).

Article CAS Google Scholar

Hu, X., Yu, S. & Chu, B. Increased effective piezoelectric response of structurally modulated P(VDF-TrFE) film devices for effective energy harvesters. Mater. Des. 192, 108700. https://doi.org/10.1016/j.matdes.2020.108700 (2020).

Article CAS Google Scholar

Wang, A., Hu, M., Zhou, L. & Qiang, X. Self-powered wearable pressure sensors with enhanced piezoelectric properties of aligned P(VDF-TrFE)/MWCNT composites for monitoring human physiological and muscle motion signs. Nanomaterials 8, 1021. https://doi.org/10.3390/nano8121021 (2018).

Article CAS PubMed Central Google Scholar

Kumar, R. et al. Heteroatom doped graphene engineering for energy storage and conversion. Mater. Today 39, 47. https://doi.org/10.1016/j.mattod.2020.04.010 (2020).

Article CAS Google Scholar

Kumar, R. et al. Nitrogen-sulfur co-doped reduced graphene oxide-nickel oxide nanoparticle composites for electromagnetic interference shielding. ACS Appl. Nano Mater. 2(7), 4626. https://doi.org/10.1021/acsanm.9b01002 (2019).

Article CAS Google Scholar

Kumar, R. et al. Microwave-assisted thin reduced graphene oxide-cobalt oxide nanoparticles as hybrids for electrode materials in supercapacitor. J. Energy Storage. 40, 102724. https://doi.org/10.1016/j.est.2021.102724 (2021).

Article Google Scholar

Cui, C., Xue, F., Hu, W. J. & Li, L. J. Two-dimensional materials with piezoelectric and ferroelectric functionalities. npj 2D Mater. Appl. 2(1), 18. https://doi.org/10.1038/s41699-018-0063-5 (2018).

Article Google Scholar

Kim, J. et al. 2-Dimensional rGO introduced PMN-PT and P(VDF-TrFE) flexible films for enhanced piezoelectric energy harvester. Appl. Surf. Sci. 494, 1000. https://doi.org/10.1016/j.apsusc.2019.06.236 (2019).

Article ADS CAS Google Scholar

Park, O. K. et al. Defect healing of reduced graphene oxide via intramolecular cross-dehydrogenative coupling. Nanotechnology 24, 185604. https://doi.org/10.1088/0957-4484/24/18/185604 (2013).

Article ADS CAS PubMed Google Scholar

Kuang, B. et al. Chemical reduction dependent dielectric properties and dielectric loss mechanism of reduced graphene oxide. Carbon 127, 209. https://doi.org/10.1016/j.carbon.2017.10.092 (2018).

Article CAS Google Scholar

Zhao, G. et al. Piezoelectric polyacrylonitrile nanofiber film-based dual-function self-powered flexible sensor. ACS Appl. Mater. Interfaces 10, 15855. https://doi.org/10.1021/acsami.8b02564 (2018).

Article CAS PubMed Google Scholar

Kumar, R. et al. An overview of recent progress in nanostructured carbon-based supercapacitor electrodes: From zero to bi-dimensional materials. Carbon 193, 298. https://doi.org/10.1016/j.carbon.2022.03.023 (2022).

Article CAS Google Scholar

Yang, J. et al. Piezoelectric enhancement of an electrospun AlN-doped P(VDF-TrFE) nanofiber membrane. Mater. Chem. Front. 5, 5679. https://doi.org/10.1039/D1QM00550B (2021).

Article CAS Google Scholar

Szewczyk, P. K. et al. Enhanced piezoelectricity of electrospun polyvinylidene fluoride fibers for energy harvesting. ACS Appl. Mater. Interfaces. 12, 13575. https://doi.org/10.1021/acsami.0c02578 (2020).

Article CAS PubMed PubMed Central Google Scholar

Mokhtari, F., Shamshirsaz, M., Latifi, M. & Foroughi, J. Nanofibers-based piezoelectric energy harvester for self-powered wearable technologies. Polymers 12, 2697. https://doi.org/10.3390/polym12112697 (2020).

Article CAS PubMed Central Google Scholar

Zaaba, N. I. et al. Synthesis of graphene oxide using modified hummers method: Solvent influence. Procedia Eng. 184, 469. https://doi.org/10.1016/j.proeng.2017.04.118 (2017).

Article CAS Google Scholar

Du, M. et al. Synthesis of nitrogen-doped reduced graphene oxide directly from nitrogen-doped graphene oxide as a high-performance lithium ion battery anode. RSC Adv. 4, 42412–42417. https://doi.org/10.1039/c4ra05544f (2014).

Article ADS CAS Google Scholar

Gevorgian, S. et al. Modeling of thin film HTS/ferroelectric interdigital capacitors. IEE Proc. Microw. Antennas Propag. 143, 397. https://doi.org/10.1049/ip-map:19960595 (1996).

Article Google Scholar

Igreja, R. & Dias, C. J. Analytical evaluation of the interdigital electrodes capacitance for a multi-layered structure. Sens. Actuators A Phys. 112, 291. https://doi.org/10.1016/j.sna.2004.01.040 (2004).

Article CAS Google Scholar

Deol, R. S. et al. A lead-free flexible energy harvesting device. Microsyst. Technol. https://doi.org/10.1007/s00542-022-05345-1 (2022).

Article Google Scholar

Chen, J. X., Li, J. W., Cheng, C. C. & Chiu, C. W. Piezoelectric property enhancement of PZT/Poly(vinylidenefluoride-co-trifluoroethylene) hybrid films for flexible piezoelectric energy harvesters. ACS Omega 7(1), 793. https://doi.org/10.1021/acsomega.1c05451 (2022).

Article CAS PubMed Google Scholar

Faraz, M., Singh, H. H. & Khare, N. A progressive strategy for harvesting mechanical energy using flexible PVDF-rGO-MoS2 nanocomposites film-based piezoelectric nanogenerator. J. Alloy. Compd. 890(15), 161840. https://doi.org/10.1016/j.jallcom.2021.161840 (2022).

Article CAS Google Scholar

Li, Y. et al. Enhanced piezoelectric performance of multi-layered flexible polyvinylidene fluoride–BaTiO3–rGO films for monitoring human body motions. J. Mater. Sci.: Mater. Electron. 33, 4291. https://doi.org/10.1007/s10854-021-07622-7 (2022).

Article CAS Google Scholar

Kim, J. H. et al. 2-Dimensional rGO introduced PMN-PT and P(VDF-TrFE) flexible films for enhanced piezoelectric energy harvester. Appl. Surf. Sci. 494(15), 1000. https://doi.org/10.1016/j.apsusc.2019.06.236 (2019).

Article ADS CAS Google Scholar

Download references

This study supported by the Human Resources Development (No.20214000000280) of the Korea Institute of Energy Technology Evaluation and Planning(KETEP) grant funded by the Korea government Ministry of Trade, Industry and Energy and was supported by the MSIT (Ministry of Science and ICT), Korea, under the ITRC (Information Technology Research Center) support program (IITP-2022-2020-0-01655) supervised by the IITP (Institute of Information and Communications Technology Planning and Evaluation).

School of Electrical and Electronic Engineering, Chung-Ang University, 84 Heukseok-Ro, Dong-Jak Gu, Seoul, 06974, Republic of Korea

Jae-Hoon Ji & Jung-Hyuk Koh

Department of Intelligent Energy and Industry, Chung-Ang University, Heukseok-ro, Seoul, 06974, Republic of Korea

Gwangseop Lee & Jung-Hyuk Koh

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

J-H.J. and J-H.K. wrote the main manuscript text. J-H.J. prepared Figs. 1, 3–5 and J-H.J. and G.L. prepared Figs. 2–9 and Tables 1, 2. All authors reviewed the manuscript.

Correspondence to Jung-Hyuk Koh.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Ji, JH., Lee, G. & Koh, JH. Synthesis of a nitrogen doped reduced graphene oxide based ceramic polymer composite nanofiber film for wearable device applications. Sci Rep 12, 15583 (2022). https://doi.org/10.1038/s41598-022-19234-0

Download citation

Received: 28 June 2022

Accepted: 25 August 2022

Published: 16 September 2022

DOI: https://doi.org/10.1038/s41598-022-19234-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.